Product Code: BA10
When used as a direct source of alumina in glazes, alumina has the effect of increasing glaze viscosity and firing range and resistance to crystallization. The crawling tendency of glazes with...
Product Code: BA1001
Derived principally from stibnite, its principle use is an opacifier in porcelain enamels. Typical analysis: Sb2O3 100% pure Melting Point 650oC It can be used in combination with rutile and...
Product Code: BA110
Premium Quality now blended in Australia. A highly plastic volcanic colloidal clay, used as a suspending agent in glazes (2-3%) but it must be added to the dry ingredients. When added to a clay...
Product Code: BA139
Primary clay which is pure, highly refractory and fires extremely white. A source of alumina and silica in glazes and a constituent of many clay bodies where whiteness is desirable e.g. bone china...
Product Code: BA150
The essential ingredient of a bone china clay, instrumental in producing its characteristic translucency. Also used as a secondary flux in glazes giving a milky quality.
Product Code: BA160
Also called Tricalcium Phosphate. It is a readily available consistent quality, for the natural bone ash. Will work well in low and high fire glazes.
Product Code: BA170
A purer form of crystalline Whiting. The main source of calcium in bodies and glazes and the most commonly used flux in high temperature glazes. It also lends hardness and durability but used in...
Product Code: BA180
A versatile and high firing pigment, dark green in the unfired state and generally producing an opaque green. In the presence of calcium it produces a grass green and with cobalt and magnesium, a...
Product Code: BA20
This 300# product is mainly used as a glaze constituant. When used as a direct source of alumina in glazes, alumina has the effect of increasing glaze viscosity and firing range and resistance to...
Product Code: BA200
This replaces Ball Clay FX which is out of production but is from the same seam of clay in Axedale near Bendigo. Highly plastic sedimentary clays used in bodies to improve workability and in...
Product Code: BA202
A blended English china clay showing some plasticity It has a low titania content, relatively high flux content and a lovely white fired color. It is excellent for making translucent throwing...
Product Code: BA204
A secondary water washed kaolin mined in Florida. It is fairly plastic and very white firing compared with most other American kaolins. It has excellent casting properties. It is not plastic...
Product Code: BA215
Used as a base for a brushing medium to impart green strength to brush work and glaze application. As a basic guide use at between 0.5 to 2% on water content. Add to warm water to dissolve and age...
Product Code: BA220
Cobalt carbonate is a fine grained material that gives more even distribution of colour than cobalt oxide. Produces an evenly textured blue glaze (1-3%) which is less intense than the oxide....
Product Code: BA230
Cobalt oxide produces an evenly textured blue glaze (1-3%) which is more intense than the carbonate. Cobalt almost always produces blues, which may vary somewhat with glaze composition, high zinc...
Product Code: BA250
Copper gives green in most fritted glazes, the colour being darker and richer in lead bearing glazes. In alkaline type glazes, the colour tends to blue, as is also the case in emulsion opacified...
Product Code: BA260
Copper gives green in most fritted glazes, the colour being darker and richer in lead bearing glazes. In alkaline type glazes, the colour tends to blue, as is also the case in emulsion opacified...
Product Code: BA280
This material is a blend of selected minerals (no fluorine) that have a chemical analysis very similar to that of the naturally occurring stone. Cornish stone is an alternative to, though not...
Brand: Walker Ceramics
Product Code: BA285
Used to mend cracks in bisqueware. Just mix with water (not too much!) to a suitable consistency to gently push into the crack. Re bisc fire to cure then decorate and glaze if required. Fires to a...
Brand: Walker Ceramics
Product Code: BA290
Iron Oxide Purple - Iron Sulphate - known as Crocus Martis FeO.Fe2O3 .FeSO4 (BA290) An impure form of iron oxide / sulphate often producing speckled effects (4-8%) The final colour obtained...
Product Code: BA30
Occasionally the preferred source of alumina in a glaze because it remains in suspension for a longer time and can be more reactive.
Product Code: BA3001
A special impure basalt feldspathoid used for giving colour and specks in bodies and glazes. This is ground through our hammer mill and will range in size from 2-3mm to dust.